ASTM C1383-15
使用冲击-回声法测量混凝土板P-波速和厚度的标准试验方法

Standard Test Method for Measuring the P-Wave Speed and the Thickness of Concrete Plates Using the Impact-Echo Method

被代替

标准号

ASTM C1383-15

发布

2015年

发布单位

美国材料与试验协会

替代标准

ASTM C1383-15(2022)

当前最新

ASTM C1383-15(2022)

 

 

引用标准

ASTM C125 ASTM C597 ASTM E1316

适用范围

4.1 This test method may be used as a substitute for, or in conjunction with, coring to determine the thickness of slabs, pavements, decks, walls, or other plate structures. There is a certain level of systematic error in the calculated thickness due to the discrete nature of the digital records that are used. The absolute systematic error depends on the plate thickness, the sampling interval, and the sampling period.

4.2 Because the wave speed can vary from point-to-point in the structure due to differences in concrete age or batch-to-batch variability, the wave speed is measured (Procedure A) at each point where a thickness determination (Procedure B) is required.

4.3 This test method is a pplicable to plate-like structures with lateral dimensions at least six times the thickness. These minimum lateral dimensions are necessary to prevent other modes3 of vibration from interfering with the identification of the thickness mode frequency in the amplitude spectrum. As explained in Note 12, the minimum lateral dimensions and acceptable sampling period are related.

4.4 The maximum and minimum thickness that can be measured is limited by the details of the testing apparatus (transducer response characteristics and the specific impactor). The limits shall be specified by manufacturer of the apparatus, and the apparatus shall not be used beyond these limits. If test equipment is assembled by the user, thickness limitations shall be established and documented.

4.5 This test method is not applicable to plate structures with overlays, such as a concrete bridge deck with an asphalt or portland cement concrete overlay. The method is based on the assumption that the concrete plate has the same P-wave speed throughout its depth.

4.6 Procedure A is performed on concrete that is air dry as high surface moisture content may affect the results.

4.7 Procedure B is applicable to a concrete plate resting on a subgrade of soil, gravel, permeable asphalt concrete, or lean portland cement concrete provided there is sufficient difference in acoustic impedance3 between the concrete and subgrade or there are enough air voids at the interface to produce measurable reflections. If these conditions are not satisfied, the waveform will be of low amplitude and the amplitude spectrum will not include a dominant peak at the frequency corresponding to the thickness (Eq 2). If the interface between the concrete and subgrade is rough, the amplitude spectrum will have a rounded peak instead of a sharp peak associated with a flat surface.

4.8 The procedures described are not influenced by traffic noise or low frequency structural vibrations set up by normal movement of traffic across a structure.

4.9 The procedures are not applicable in the presence of mechanical noise created by equipment impacting (jack hammers, sounding wi......

案例分享：铁路隧道衬砌阵列式超声无损检测

现阶段，对于隧道质量检测常用的手段方法主要有以下几种：电磁波法：雷达检测衬砌（支护）厚度、衬砌背后的回填密实度、衬砌内部缺陷和衬砌内部钢架、钢筋等分布光学法：三维激光扫描检测新建和运营隧道净空断面、衬砌表面平整度、衬砌内钢筋布置、（应浇筑）衬砌厚度等冲击弹性波法：冲击回波法检测衬砌混凝土厚度、密实性、内部缺陷、脱空及层间结合状况等超声法：阵列超声检测衬砌以及密集钢筋段衬砌混凝土裂缝、厚度、内部缺陷等回弹法...

SR-9型混凝土回弹测厚仪的操作规程及试验使用说明

型号区分：YX-SR-9系列混凝土测厚仪分为单通道与双通道两款混凝土测厚仪YX-SR-9混凝土测厚仪 〖单通道测量 真彩液晶触摸屏〗测量方式为采用钻孔取芯测试回弹波速YX-SR-9混凝土测厚仪 〖双通道测量 真彩液晶触摸屏〗测量方式为：信号采集，时差法测试波速，无需钻孔取芯测波速SR-9型混凝土回弹测厚仪的操作规程及试验使用说明应用范围(1) 公路、桥梁路面厚度测试；(2) 机场跑道混凝土厚度测试；...

混凝土测厚仪的产品特点技术指标与操作注意事项

混凝土测厚仪的产品特点技术指标与操作注意事项  型号区分：YX-HCH-01/02系列混凝土测厚仪分为单通道与双通道两款混凝土测厚仪YX-HCH-01混凝土测厚仪 〖单通道测量 真彩液晶触摸屏〗测量方式为采用钻孔取芯测试回弹波速YX-HCH-02混凝土测厚仪 〖双通道测量 真彩液晶触摸屏〗测量方式为：信号采集，时差法测试波速，无需钻孔取芯测波速混凝土测厚仪的产品特点技术指标与操作注意事项  应用范围...

YX-HCH-02双通道混凝土测厚仪如何操作及测厚仪测量精度

YX-HCH-01混凝土测厚仪〖单通道测量 真彩液晶触摸屏〗测量方式为采用钻孔取芯测试回弹波速 YX-HCH-02混凝土测厚仪〖双通道测量 真彩液晶触摸屏〗测量方式为：信号采集，时差法测试波速，无需钻孔取芯测试应用范围(1) 公路、桥梁路面厚度测试；(2) 机场跑道混凝土厚度测试；(3) 隧道衬砌厚度测试；(4) 公路边坡混凝土厚度测试；(5) 防洪堤坝、大坝混凝土厚度测试。...