5.1 Before proceeding with these test methods, reference should be made to the specification of the material being tested. Any test specimen preparation, conditioning, dimensions, and testing parameters covered in the materials specification shall take precedence over those mentioned in these test methods. If there is no material specification, then the default conditions apply.
5.2 The pendulum impact test indicates the energy to break standard test specimens of specified size under stipulated parameters of specimen mounting, notching, and pendulum velocity-at-impact.
5.3 The energy lost by the pendulum during the breakage of the specimen is the sum of the following:
5.3.1 Energy to initiate fracture of the specimen;
5.3.2 Energy to propagate the fracture across the specimen;
5.3.3 Energy to throw the free end (or ends) of the broken specimen (“toss correction”);
5.3.4 Energy to bend the specimen;
5.3.5 Energy to produce vibration in the pendulum arm;
5.3.6 Energy to produce vibration or horizontal movement of the machine frame or base;
5.3.7 Energy to overcome friction in the pendulum bearing and in the indicating mechanism, and to overcome windage (pendulum air drag);
5.3.8 Energy to indent or deform plastically the specimen at the line of impact; and
5.3.9 Energy to overcome the friction caused by the rubbing of the striker (or other part of the pendulum) over the face of the bent specimen.
5.4 For relatively brittle materials, for which fracture propagation energy is small in comparison with the fracture initiation energy, the indicated impact energy absorbed is, for all practical purposes, the sum of factors 5.3.1 and 5.3.3. The toss correction (see 5.3.3) may represent a very large fraction of the total energy absorbed when testing relatively dense and brittle materials. Test Method C shall be used for materials that have an Izod impact resistance of less than 27 J/m (0.5 ft·lbf/in.). (See Appendix X4 for optional units.) The toss correction obtained in Test Method C is only an approximation of the toss error, since the rotational and rectilinear velocities may not be the same during the re-toss of the specimen as for the original toss, and because stored stresses in the specimen may have been released as kinetic energy during the specimen fracture.
5.5 For tough, ductile, fiber filled, or cloth-laminated materials, the fr......
因为测试在高速下进行,杂质、气泡、微小裂纹等影响极大,所以对测定前后试样情况须 悬臂梁冲击试验机主要用于硬质塑料、增强尼龙、玻璃钢、陶瓷、铸石、电绝缘材料等非金属材料冲击韧性的测定。悬臂梁冲击试验机符合GB/T1843《塑料悬臂梁冲击试验方法》以及ISO180、GB/T2611、JB/T8761标准的要求。...
电子式冲击试验机采用高精度编码器技术,具有精度高、稳定性好和测量范围大等特点,数字化测量显示冲击强度及平均值,能量损失自动修正,打印试验报告等功能。该机符合国际标准ISO180—1992《塑料—硬质材料悬臂梁冲击强度的测定》;国家标准GB/T1843—1996《硬质塑料悬臂梁冲击试验方法》、机械行业标准JB/T8761—1998《塑料悬臂梁冲击试验机》。...
本悬臂梁冲击试验机主要用于硬质塑料、增强尼龙、玻璃钢、陶瓷,铸石、电绝缘材料等非金属材料冲击韧性的测定。是化工行业、科研单位、大专院校,质量检测等部门理想的测试设备。本冲击试验机是采用微计算机技术研制生产的智能化数显式冲击试验机。先进之处在于它能够自动修正摩擦和风阻所带来的能量损失,摆脱了能量由于阻力影响而进行修正的数值图表。(试样断裂后摆锤剩余能量的检测和能量损失的修正在冲击过程中一次完成)。...
符合国际标准ISO180—1992《塑料—硬质材料悬臂梁冲击强度的测定》;国家标准GB/T1843—1996《硬质塑料悬臂梁冲击试验方法》、机械行业标准JB/T8761—1998《塑料悬臂梁冲击试验机》。...