25.220.20;77.120.10 标准查询与下载

BS EN ISO 6581:2018 铝及其合金的阳极氧化 彩色阳极氧化涂层耐紫外光和耐热性比较牢度的测定

Anodizing of aluminium and its alloys. Determination of the comparative fastness to ultraviolet light and heat of coloured anodic oxidation coatings

BS EN ISO 2085:2018 铝及其合金的阳极氧化 检查薄阳极氧化涂层的连续性 硫酸铜测试

Anodizing of aluminium and its alloys. Check for continuity of thin anodic oxidation coatings. Copper sulfate test

JIS H 8687:2013 铝和铝合金阳极氧化.电强度测定

This Standard specifies the breakdown test and the withstand voltage test of sealed anodic oxidation coatings (hereafter referred to as "coatings") on aluminium and aluminium alloy products (hereafter referred to as "products").

Anodizing of aluminium and its alloys.Determination of electric strength

JIS H 8688:2013 铝和铝合金阳极氧化.阳极氧化涂层每一单位面积质量(表面密度)的测定

This Standard specifies a gravimetric method for determining the mass per unit area (surface density) of anodic oxidation coatings (hereafter referred to as "coatings") on products of aluminium and its alloys (hereafter referred to as "products").

Anodizing of aluminium and its alloys -- Determination of mass per unit area (surface density) of anodic oxidation coatings

JIS H 8683-3:2013 铝和铝合金的阳极氧化.阳极氧化膜封孔质量的评估.第3部分:导纳测量法

Anodizing of aluminium and its alloys.Assessment of quality of sealed anodic oxidation coatings .Part 3: Measurement of admittance

JIS H 8682-3:2013 铝和铝合金的阳极氧化.阳极氧化涂层耐磨性测量.第3部分:耐落沙磨损试验

Anodizing of aluminium and its alloys.Measurement of abrasion resistance of anodic oxidation coatings .Part 3: Falling sand abrasion resistance test

JIS H 8683-1:2013 铝和铝合金的阳极氧化.封孔后的阳极氧化膜吸收能力损失的评估.第1部分:酸处理后的染斑试验

Anodizing of aluminium and its alloys.Estimation of loss of absorptive power of anodic oxidation coatings after sealing.Part 1: Dye-spot test with prior acid treatment

JIS H 8683-2:2013 铝和铝合金的阳极氧化.阳极氧化膜封孔质量的评估.第2部分:浸入磷酸/铬酸溶液后质量损失测量法

Anodizing of aluminium and its alloys -- Assessment of quality of sealed anodic oxidation coatings -- Part 2: Measurement of the loss of mass after immersion in phosphoric acid/chromic acid solution

JIS H 8682-1:2013 铝和铝合金的阳极氧化.阳极氧化涂层耐磨性测量.第1部分:摩擦轮磨耗耐磨性试验

Anodizing of aluminium and its alloys.Measurement of abrasion resistance of anodic oxidation coatings .Part 1: Abrasive-wheel-wear abrasion resistance test

JIS H 8682-2:2013 铝和铝合金的阳极氧化.阳极氧化涂层耐磨性测量.第2部分:喷沙耐磨性试验

Anodizing of aluminium and its alloys.Measurement of abrasion resistance of anodic oxidation coatings.Part 2: Abrasive jet abrasion resistance test

KS D 8314-1-2011 铝和铝合金的阳极氧化涂层的耐磨性试验方法.第1部分:车轮磨损试验

이 표준은 알루미늄 및 알루미늄 합금의 제품(이하, 제품이라 한다.)에 실시한 5 μm 이

Test methods for abrasion resistance of anodic oxide coatings on aluminium and aluminium alloys-Part 1:Wheel wear test

BS EN ISO 2106:2011 铝及铝合金阳极氧化.阳极氧化涂层每单位面积质量(表面密度)的测定.重量法

This International Standard specifies a gravimetric method for determining the mass per unit area (surface density) of anodic oxidation coatings on aluminium and its alloys. The method is applicable to all oxidation coatings formed by anodizing aluminium and its alloys, either cast or wrought, and is suitable for most aluminium alloys, except those in which the copper content is greater than 6 %. NOTE 1 A high content of copper in the alloy can lead to increased dissolution of the basis aluminium. NOTE 2 If the thickness is known with sufficient precision (for example, using the method specified in ISO 2128), determination of the mass per unit area (surface density) of the coatings will enable its apparent density to be calculated. Conversely, if the conditions of application of the coating and its density are known, the determination of its mass per unit area (surface density) can permit calculation of the average mass and an approximate evaluation of the thickness (see the Note in Clause 6).

Anodizing of aluminium and its alloys. Determination of mass per unit area (surface density) of anodic oxidation coatings. Gravimetric method

BS EN ISO 2085:2010 铝和铝合金的阳极氧化.稀薄阳极氧化涂层连续性处理.硫酸铜试验

This International Standard specifies a method for checking the continuity of thin anodic oxidation coatings on aluminium and its alloys by a copper sulfate contact test. The use of this method is limited to anodic oxidation coatings of thickness less than 5 μm, or coatings that have been deformed. NOTE The method described enables a rapid check to be made for the continuity of a thin coating of aluminium oxidation on aluminium and its alloys. In cases of doubt regarding a visible fault on the surface of a coating, the use of this method makes it possible to verify whether the fault corresponds to a local gap in the coating which exposes bare metal.

Anodizing of aluminium and its alloys. Check for continuity of thin anodic oxidation coatings. Copper sulfate test

BS EN ISO 3211:2010 铝和铝合金的阳极氧化.阳极氧化涂层变形裂解耐受性评定

This International Standard specifies an empirical method for assessing the resistance of anodic oxidation coatings to cracking by deformation. The method is applicable particularly to sheet material with anodic oxidation coatings of thickness less than 5 μm, and is useful for development purposes. NOTE If the test piece is thick, even more than 5 μm of coating can be measured (see Clause 6).

Anodizing of aluminium and its alloys. Assessment of resistance of anodic oxidation coatings to cracking by deformation

BS EN ISO 7759:2010 铝及其合金的阳极氧化.用滤色光度测角计或光度测角计测量铝表面的反射特性

This International Standard specifies a method for the measurement of the reflectance characteristics of highgloss anodized aluminium surfaces. The method described is also suitable for the measurement of the reflectance characteristics of other highgloss metal surfaces. The method is not suitable for diffuse-finish metal surfaces and does not measure colour.

Anodizing of aluminium and its alloys. Measurement of reflectance characteristics of aluminium surfaces using a goniophotometer or an abridged goniophotometer

BS EN ISO 6581:2010 铝和铝合金阳极氧化.有色阳极氧化涂层对紫外线和高温的比较牢固度测定

This International Standard specifies a comparative method for the determination of the fastness of coloured anodic oxidation coatings to ultraviolet (UV) light and heat. The method is not suitable for testing coloured anodic oxidation coatings that are heat sensitive. NOTE Dark-coloured test pieces will normally reach the highest temperatures.

Anodizing of aluminium and its alloys. Determination of the comparative fastness to ultraviolet light and heat of coloured anodic oxidation coatings

JIS H 8602:2010 铝及铝合金的阳极氧化和有机涂层的复合覆层

This Japanese Industrial Standard specifies the combined coatings of anodic oxide and organic coatings (hereafter referred to as "combined castings")executed on the base metal of wrought product of aluminium and aluminium alloys for pruposes of corrosion prevention,good appearance, etc.

Combined coatings of anodic oxide and organic coatings on aluminium and aluminium alloys

BS EN 12373-7:2002 铝和铝合金.阳极化处理.通过测量浸入预先进行酸处理的磷酸/铬酸溶液中后的重量损失来评价密封阳极氧化涂层的质量

This European Standard specifies a method of assessing the quality of sealed anodic oxidation coatings on aluminium and its alloys by measurement of the loss of mass after immersion in phosphoric acid/chromic acid solution with prior acid treatment. A related standard (EN 12373-61)) describes the same method used without prior acid treatment. The method is particularly applicable to anodic oxidation coatings intended for architectural purposes. For less severe applications, the method described in EN 12373-61) may be more suitable. The method is not applicable to: ? hard-type anodic oxidation coatings which normally are not sealed; ? anodic oxidation coatings that have been sealed only in dichromate solutions; ? anodic oxidation coatings produced in chromic acid solutions; ? anodic oxidation coatings that have undergone a treatment to render them hydrophobic. The method is destructive and can serve as a reference method in case of doubt or dispute regarding the results of the test for loss of absorptive power (EN 12373-41)), or the measurement of admittance (EN 12373-51)).

Aluminium and aluminium alloys - Anodizing - Assessment of quality of sealed anodic oxidation coatings by measurement of the loss of mass after immersion in phosphoric acid/chromic acid solution with prior acid treatment

SANS 999:2007 铝表面阳极化处理层（建筑应用）

Covers three grades of anodized coating that are used to impart protective, decorative or functional properties to the surfaces of aluminium alloys and that are commonly used for architectural applications.

Anodized coatings on aluminium (for architectural applications)

SANS 1407:2007 铝阳极化镀层（普通用）

Covers six grades of anodized (anodic oxide) coating that are used to improve the resistance to corrosion of aluminium and aluminium alloys in general applications.

Anodized coatings on aluminium (for general applications)