GSO ISO 75-2:2015
塑料 负载变形温度的测定 第2部分：塑料和硬橡胶

Plastics -- Determination of temperature of deflection under load -- Part 2: Plastics and ebonite

GSO ISO 75-2:2015 发布历史

GSO ISO 75-2:2015由GSO 发布于 2015-09-03。

GSO ISO 75-2:2015在国际标准分类中归属于: 83.080.10 热固性塑料。

GSO ISO 75-2:2015 塑料 负载变形温度的测定 第2部分：塑料和硬橡胶的最新版本是哪一版？

最新版本是 GSO ISO 75-2:2015 。

GSO ISO 75-2:2015的历代版本如下：

• 2015年 GSO ISO 75-2:2015 塑料 负载变形温度的测定 第2部分：塑料和硬橡胶

This part of ISO 75 specifies three methods, using different values of constant flexural stress, which can be used for the determination of the temperature of deflection under load of plastics (including filled plastics and fibre-reinforced plastics in which the fibre length, prior to processing, is up to 7,5 mm) and ebonite: • — method A, using a flexural stress of 1,80 MPa; • — method B, using a flexural stress of 0,45 MPa; • — method C, using a flexural stress of 8,00 MPa. The standard deflection, Δs, used to determine the temperature of deflection under load corresponds to a flexural-strain increase, Δεf, defined in this part of ISO 75. The initial flexural strain due to the loading of the specimen at room temperature is neither specified nor measured in this part of ISO 75. The ratio of this flexural-strain increase to the initial flexural strain depends on the modulus of elasticity, at room temperature, of the material under test. This method is, therefore, only suitable for comparing the temperatures of deflection of materials with similar room-temperature elastic properties. NOTE 1 The methods give better reproducibility with amorphous plastics than with semi-crystalline ones. With some materials, it can be necessary to anneal the test specimens to obtain reliable results. Annealing procedures, if used, generally result in an increase in the temperature of deflection under load (see 6.6). NOTE 2 For additional information, see ISO 75-1:2013, Clause 1.

标准号

GSO ISO 75-2:2015

发布

2015年

发布单位

GSO

当前最新

GSO ISO 75-2:2015

 

 

GSO ISO 75-2:2015相似标准

推荐