ASTM C1674-23
环境温度下具有工程孔隙率（蜂窝状孔道）的先进陶瓷的弯曲强度的标准测试方法

Standard Test Method for Flexural Strength of Advanced Ceramics with Engineered Porosity (Honeycomb Cellular Channels) at Ambient Temperatures

标准号

ASTM C1674-23

发布

2023年

发布单位

美国材料与试验协会

当前最新

ASTM C1674-23

 

 

引用标准

ASTM C1145 ASTM C1161 ASTM C1198 ASTM C1239 ASTM C1259 ASTM C1292 ASTM C1341 ASTM C1368 ASTM C1525 ASTM C1576 ASTM C373 ASTM D2344/D2344M ASTM E177 ASTM E337 ASTM E4 ASTM E6 ASTM E691 IEEE/ASTM SI 10

适用范围

1.1 This test method covers the determination of the flexural strength (modulus of rupture in bending) at ambient conditions of advanced ceramic structures with 2-dimensional honeycomb channel architectures. 1.2 The test method is focused on engineered ceramic components with longitudinal hollow channels, commonly called “honeycomb” channels (see Fig. 1). The components generally have 30 % or more porosity and the cross-sectional dimensions of the honeycomb channels are on the order of 1 mm or greater. Ceramics with these honeycomb structures are used in a wide range of applications (catalytic conversion supports (1),2 high temperature filters (2, 3), combustion burner plates (4), energy absorption and damping (5), etc.). The honeycomb ceramics can be made in a range of ceramic compositions—alumina, cordierite, zirconia, spinel, mullite, silicon carbide, silicon nitride, graphite, and carbon. The components are produced in a variety of geometries (blocks, plates, cylinders, rods, rings). 1.3 The test method describes two test specimen geometries for determining the flexural strength (modulus of rupture) for a porous honeycomb ceramic test specimen (see Fig. 2): 1.3.1 Test Method A—A 4-point or 3-point bending test with user-defined specimen geometries, and 1.3.2 Test Method B—A 4-point-1⁄4 point bending test with a defined rectangular specimen geometry (13 mm × 25 mm × > 116 mm) and a 90 mm outer support span geometry suitable for cordierite and silicon carbide honeycombs with small cell sizes. 1.4 The test specimens are stressed to failure and the breaking force value, specimen and cell dimensions, and loading geometry data are used to calculate a nominal beam strength, a wall fracture strength, and a honeycomb structure strength. 1.5 Test results are used for material and structural development, product characterization, design data, quality control, and engineering/production specifications. 1.6 The test method is meant for ceramic materials that are linear-elastic to failure in tension. The test method is not applicable to polymer or metallic porous structures that fail in an elastomeric or an elastic-ductile manner. 1.7 The test method is defined for ambient testing temperatures. No directions are provided for testing at elevated or cryogenic temperatures. 1.8 The values stated in SI units are to be regarded as standard (IEEE/ASTM SI 10). English units are sparsely used in this standard for product definitions and tool descriptions, per the cited references and common practice in the US automotive industry. 1.9 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.10 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ASTM C1674-23相似标准

推荐