镁合金铸件 砂 3.3Th 2.1Zn 0.75Zr（HZ32A-T5）沉淀热处理（UNS M13320）
Magnesium Alloy Castings@ Sand 3.3Th - 2.1Zn - 0.75Zr (HZ32A-T5) Precipitation Heat Treated (UNS M13320)
2006-06
购买全文，请联系:
- 标准号
- SAE AMS4447F-2006
- 发布
- 2006年
- 发布单位
- SAE - SAE International
- 当前最新
- SAE AMS4447F-2006
- 适用范围
- Form: This specification covers a magnesium alloy in the form of sand castings. Application: Primarily for parts operating in service at 400?? 600??(205?? 315??. Material covered by this specification is radioactive. All applicable rules and regulations@ including those of the Nuclear Regulatory Agency@ pertaining to handling of radioactive material and all licensing provisions for use of such material should be observed.
SAE AMS4447F-2006相似标准
SAE AMS4447D-1985 镁合金铸件 SAND 3.3Th 2.1Zn 0.75Zr（HZ32A-T5）沉淀热处理（UNS M13320）
SAE AMS4447E-2000 镁合金铸件，砂 3.3Th 2.1Zn 0.75Zr（HZ32A-T5）沉淀热处理
SAE AMS4447C-1979 镁合金铸件 SAND 3.3Th 2.1Zn 0.75Zr（HZ32A-T5）（UNS M13320）
SAE AMS4447E-1985 沉淀热处理的砂型铸造3.3Th 2.1Zn 0.75Zr镁合金铸件
SAE AMS4447A-1965 镁合金铸件 SAND 3.3Th 2.1Zn 0.8Zr（HZ32A-T5）时效处理
推荐
【收藏】镁合金热处理的介绍
常用的措施包括特定的加热和冷却工艺，也就是热处理。钢铁的淬火，为的是快速冷却以保持其高温相，从而达到所需要的性能。对于镁合金，常采用的热处理方式包括：均匀化退火（扩散退火）、固溶（淬火）（T4）、时效（T5）、固溶+时效（T6）、热水淬火+时效（T61）、去应力退火、完全退火等。这里做以下方面简要介绍：1、均质化退火。其目的是消除铸件在凝固过程中形成的晶内偏析。那么，晶内偏析是如何形成的呢？...
镁合金热处理工艺及研究
多数镁合金都可通过热处理来改善或调整材料的力学性能和加工性能。镁合金能否通过热处理强化完全取决于合金元素的固溶度是否随温度变化。当合金元素的固溶度随温度变化时，镁合金可以进行热处理强化。镁合金的常规热处理工艺分为退火和固溶时效两大类。镁合金热处理强化的特点是：合金元素的扩散和合金相的分解过程极其缓慢，因此固溶和时效处理时需要保持较长的时间。...