ISO 22858:2020
金属和合金腐蚀电化学测量大气腐蚀监测试验方法
Corrosion of metals and alloys — Electrochemical measurements — Test method for monitoring atmospheric corrosion
- 标准号
- ISO 22858:2020
- 发布
- 2020年
- 发布单位
- 国际标准化组织
- 当前最新
- ISO 22858:2020
- 引用标准
- ISO 4618 ISO 4628 (all parts) ISO 8044 ISO 9223
- 适用范围
- This document specifies a test method for atmospheric corrosion measurements, using two-electrode electrochemical sensors. It is applicable to measurements of the corrosion rate of uncoupled metal surfaces (i.e. “free” corrosion rate), galvanic corrosion rate, conductance of thin film solutions and barrier properties of organic coatings. It specifies electrochemical sensors that are used with or without organic coatings. The sensors are applicable to corrosion measurements made in laboratory test chambers, outdoor exposure sites and service environments.
ISO 22858:2020相似标准
推荐
电化学显微镜原理及应用
电化学显微镜的应用： 不锈钢和铝等材料的点蚀检测、成长过程在线监测等； 有机和金属涂层缺陷和完整性研究； 金属/有机涂层界面的腐蚀的机制与检测； 有机涂层的剥离和脱落机制； 钝化处理的不锈钢焊接热影响区的电位分布； 干湿循环的碳钢和不锈钢的阴极区和阳极区的分布行为； 薄液层下氧还原反应和金属的腐蚀过程的特征； 模拟不同大气环境的腐蚀电位在线监测； 铝合金等材料在大气环境中局部腐蚀敏感性...
电化学显微镜特点及应用分析
不锈钢和铝等材料的点蚀检测、成长过程在线监测等；有机和金属涂层缺陷和完整性研究；金属/有机涂层界面的腐蚀的机制与检测；有机涂层的剥离和脱落机制；钝化处理的不锈钢焊接热影响区的电位分布；干湿循环的碳钢和不锈钢的阴极区和阳极区的分布行为；薄液层下氧还原反应和金属的腐蚀过程的特征；模拟不同大气环境的腐蚀电位在线监测；铝合金等材料在大气环境中局部腐蚀敏感性；铝合金的丝状腐蚀（filiform corrosion...
电化学法测量腐蚀速率的适用范围
电化学测试技术因具有操作简单、测量耗时短、对材料损害小、测量结果精确和获得的电极腐蚀动力学信息全面等优点，被广泛应用于腐蚀科学的研究中。1、开路电位法将金属或合金浸泡在腐蚀溶液中， 连接电化学测量电路，在没有外电流通过的情况下，测得的稳定电位即为开路电位。 通过测量开路电位可研究金属或合金的腐蚀和钝化情况，且方法操作简单，由于没有电流通过，不会造成极化，也有利于保护材料。...
应力腐蚀断裂你知道有多少
一般认为纯金属不易发生应力腐蚀开裂，合金比纯金属更易发生应力腐蚀开裂。下表列出了各种合金风应力腐蚀开裂的环境介质体系，介质有特点：即金属或合金可形成纯化膜，弹介质中有有破坏纯化膜完整性的离子存在。而且介质中的有害物质浓度往往很低，如大气中微量的H2S和NH3可分别引起钢和铜合金的应力腐蚀开裂。空气中少量NH3是鼻子嗅不到的，却能引起黄铜的氨脆。...