BS 2782-3 Method 352F-1996
塑料试验方法.第3部分:机械特性.试验方法352F:自由落体法测定抗冲击(仪器穿孔试验)
Methods of testing plastics - Mechanical properties - Determination of impact resistance by the free-falling dart method (instrumented puncture test)
- 标准号
- BS 2782-3 Method 352F-1996
- 发布日期
- 1996年09月15日
- 实施日期
- 1996年09月15日
- 废止日期
- 无
- 中国标准分类号
- G31
- 国际标准分类号
- 83.140.10
- 发布单位
- 英国标准学会
- 适用范围
- 1 The impact-penetration test described in the two parts of this International Standard is used for the assessment of plastic films and thin sheets (herein-after referred to as films) under an impact stress ap-plied at right angles to the plane of the film. 2 Part 1 of this International Standard can be used if it is sufficient to characterize the impact behaviour of the film by an impact-failure energy. Part 2 is used if a force-deformation or a force-time diagram, re-corded at practically constant velocity of the striker, is necessary for characterization of the impact behav-iour. This applies if: — measured quantities derivable only from this dia-gram are required or — only a small number of test specimens are avail-able. 3 The test method is applicable to films of up to 1 mm thickness and makes it possible to compare impact-penetration forces, biaxial deformabilities and energy-absorption capacities of films. Furthermore, if required, the transition region between brittle and tough behaviour of the film under the conditions of testing can be determined by varying the temperature or the penetration velocity or the relative humidity (see also annex B). NOTE 1 For thicknesses greater than 1 mm, ISO 6603-2 should be used. 4 The test results are comparable only if the con-ditions for preparation of specimens, their thickness and surfaces, and the test conditions are identical. Comprehensive evaluation of the reaction to impact stress requires that the determinations are made as functions of deformation rate and temperature for different material variables, such as crystallinity and moisture content.