SAE AMS 3349C-1993
1100psi(7.58MPa)抗拉强度的高弹性硅酮橡胶.65-75

Silicone (VMQ) Rubber 1100 psi (7.58 MPa) Tensile Strength, High Resiliency 65 - 75

SAE AMS 3349C-1993 发布历史

This specification covers a silicone (VMQ) rubber in the form of sheet, strip, tubing, molded shapes and extrusions. These products have been used typically for parts required to operate or seal from -65 to +205 degrees C (-85 to +401 degrees F), compounded especially for high strength and resiliency, but usage is not limited to such applications. Silicone elastomer is resistant to deterioration by weathering and aircraft piston engine oil and remains flexible over the temperature range noted. This material is not normally suitable for use in contact with gasoline or aromatic fuels and low-aniline-point petroleum-base fluids due to excessive swelling of the elastomer.

SAE AMS 3349C-1993由美国机动车工程师协会 US-SAE 发布于 1993。

SAE AMS 3349C-1993 在中国标准分类中归属于: G35 合成橡胶，在国际标准分类中归属于: 49.025.40 橡胶和塑料。

SAE AMS 3349C-1993的历代版本如下：

• 1993年 SAE AMS 3349C-1993 1100psi(7.58MPa)抗拉强度的高弹性硅酮橡胶.65-75

SAE AMS 3349C-1993 1100psi(7.58MPa)抗拉强度的高弹性硅酮橡胶.65-75 于 2014-05-27 变更为 SAE AMS 3349D-2014 1100psi(7.58MPa)抗拉强度的高弹性硅酮橡胶.65-75。

非常抱歉，我们暂时无法提供预览，您可以试试： 免费下载 SAE AMS 3349C-1993 前三页，或者稍后再访问。

注意： 点击下载后，生成下载文件时间比较长，请耐心等待......

标准号

SAE AMS 3349C-1993

发布日期

1993年

实施日期

废止日期

无

中国标准分类号

G35

国际标准分类号

49.025.40

发布单位

US-SAE

代替标准

SAE AMS 3349D-2014

适用范围

This specification covers a silicone (VMQ) rubber in the form of sheet, strip, tubing, molded shapes and extrusions. These products have been used typically for parts required to operate or seal from -65 to +205 degrees C (-85 to +401 degrees F), compounded especially for high strength and resiliency, but usage is not limited to such applications. Silicone elastomer is resistant to deterioration by weathering and aircraft piston engine oil and remains flexible over the temperature range noted. This material is not normally suitable for use in contact with gasoline or aromatic fuels and low-aniline-point petroleum-base fluids due to excessive swelling of the elastomer.