ANSI/ASTM E643-1984
金属薄板材球击变形试验方法

Test Method for Ball Punch Deformation of Metallic Sheet Material

ANSI/ASTM E643-1984 发布历史

This test method covers the procedure for conducting the ball punch deformation test for metallic sheet materials intended for forming applications. The test applies to specimens with thicknesses between 0.008 and 0.080 in. (0.20 and 2.00 mm). The values stated in inch-pound units are to be regarded as the standard. Note 1-The ball punch deformation test is intended to replace the Olsen cup test by standardizing many of the test parameters that previously have been left to the discretion of the testing laboratory. Note 2-The modified Erichsen test has been standardized in Europe. The main differences between the ball punch deformation test and the Erichsen test are the diameters of the penetrator and the dies. Erichsen cup heights are given in SI units. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ANSI/ASTM E643-1984由美国国家标准学会 US-ANSI 发布于 1984。

ANSI/ASTM E643-1984 在中国标准分类中归属于: H23 金属工艺性能试验方法，在国际标准分类中归属于: 77.040.10 金属材料机械试验。

ANSI/ASTM E643-1984的历代版本如下：

• 1984年 ANSI/ASTM E643-1984 金属薄板材球击变形试验方法

非常抱歉，我们暂时无法提供预览，您可以试试： 免费下载 ANSI/ASTM E643-1984 前三页，或者稍后再访问。

注意： 点击下载后，生成下载文件时间比较长，请耐心等待......

标准号

ANSI/ASTM E643-1984

发布日期

1984年

实施日期

废止日期

无

中国标准分类号

H23

国际标准分类号

77.040.10

发布单位

US-ANSI

适用范围

This test method covers the procedure for conducting the ball punch deformation test for metallic sheet materials intended for forming applications. The test applies to specimens with thicknesses between 0.008 and 0.080 in. (0.20 and 2.00 mm). The values stated in inch-pound units are to be regarded as the standard. Note 1-The ball punch deformation test is intended to replace the Olsen cup test by standardizing many of the test parameters that previously have been left to the discretion of the testing laboratory. Note 2-The modified Erichsen test has been standardized in Europe. The main differences between the ball punch deformation test and the Erichsen test are the diameters of the penetrator and the dies. Erichsen cup heights are given in SI units. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.