This part of ISO 16276 specifies procedures for assessing the fracture strength of a protective paint coating of any thickness on a steel substrate of thickness not less than 10 mm. The procedures given in this part of ISO 16276 are based on methods used with different types of pull-off test equipment. The results obtained using such different types of equipment are not comparable. NOTE 1 Substrates of less than 10 mm in thickness can be tested if they are strengthened by the sandwich technique (see ISO 4624) or by the nature of the structure (e.g. I-beam or backing-plate). Otherwise, test panels with a thickness of at least 10 mm coated in the same way as the structure can be,used, or the method specified ISO 16276-2 can be used. This part of ISO 16276 is only applicable if a fracture strength value is specified, together with the type of test equipment and the manufacturer of the equipment. Usually, this information is included in contract documentation. NOTE 2 A value for the fracture strength is only meaningful if the requirements concerning the ambient conditions (see 6.4.2) are met. This part of ISO 16276 also specifies suitable equipment and defines inspection areas, sampling plans and acceptance/rejection criteria. It does not give any values of the fracture strength of different protective paint coatings.
DIN EN ISO 16276-1-2007由德国标准化学会 DE-DIN 发布于 2007-08。
DIN EN ISO 16276-1-2007 在中国标准分类中归属于: A29 材料防护,在国际标准分类中归属于: 87.040 涂料和清漆,91.080.10 金属结构。
* 在 DIN EN ISO 16276-1-2007 发布之后有更新,请注意新发布标准的变化。
非常抱歉,我们暂时无法提供预览,您可以试试: 免费下载 DIN EN ISO 16276-1-2007 前三页,或者稍后再访问。
点击下载后,生成下载文件时间比较长,请耐心等待......
Copyright ©2007-2022 ANTPEDIA, All Rights Reserved
京ICP备07018254号 京公网安备1101085018 电信与信息服务业务经营许可证:京ICP证110310号