ASTM C1054-2003(2008)
压制的和干燥塑性耐火材料及捣实混合样品的标准实施规范

tandard Practice for Pressing and Drying Refractory Plastic and Ramming Mix Specimens

ASTM C1054-2003(2008) 发布历史

This practice is useful for producing uniform specimens of refractory plastics and ramming mixes for use in standard ASTM tests. Samples thus formed may be used for referee testing when setting specifications between producer and user. Forming parameters such as sample size, workability, and forming pressure should be agreed upon and specified in the report when referee testing.

This practice is applicable for preparing test specimens of various sizes. Note that 9 by 4x00BD; by 2x00BD; in. (228 by 114 by 64-mm) samples, because of their large cross-section, have a greater tendency to form flaws during pressing, handling, and drying than smaller cross-sectional samples.

Other tests for which these specimens may be used encompass, but are not limited to, the following ASTM standards: Method C 16, Test Methods C 20, Test Method C 113, Test Methods C 133, Test Method C 179, Test Method C 288, Test Method C 417, Test Method C 577, Test Method C 583, Test Method C 704, Test Methods C 830, Test Method C 832, Practice C 874, Test Method C 885, and Test Method C 914.

A purpose of this practice is to minimize flaws in pressed specimens. It is not intended to duplicate all field installation conditions.

Variations in workability as determined by Test Method C 181 can significantly affect the number of flaws contained in a specimen. For comparison testing between two laboratories, the workability level should be established by mutual agreement.

This practice is not intended for preparing specimens of basic ramming mixes, anhydrous tap-hole mixes, nor resin bonded mixes.

1.1 This practice covers the pressing and drying of chemically and nonchemically bonded aluminum-silicate and high alumina plastic and ramming mix refractory specimens classified in accordance with Classification C 673.

1.2 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ASTM C1054-2003(2008)由美国材料与试验协会 US-ASTM 发布于 2003。

ASTM C1054-2003(2008) 在中国标准分类中归属于: Q40 耐火材料综合。

ASTM C1054-2003(2008)的历代版本如下：

• 2003年04月10日 ASTM C1054-03 耐火塑料和捣碎混合物的压制和干燥标准实践
• 2008年03月01日 ASTM C1054-03(2008) 耐火塑料和捣打混合物试样的压制和干燥标准实施规程
• 2013年04月01日 ASTM C1054-13 耐火塑料和捣碎混合物的压制和干燥标准实践
• 2018年10月01日 ASTM C1054-18 耐火塑料和捣碎混合物的压制和干燥标准实践
• 1985年 ASTM C1054-1985(1995) 耐火塑料和填充料试样压制和干燥的标准规程
• 2003年 ASTM C1054-2003 压制和干燥耐火塑料及夯实混合样件的标准实施规程
• 2003年 ASTM C1054-2003(2008) 压制的和干燥塑性耐火材料及捣实混合样品的标准实施规范
• 2013年 ASTM C1054-2013 压制的和干燥塑性耐火材料及捣实混合试样的标准实施规程
• 1995年01月01日 ASTM C1054-85(1995) 耐火塑料和捣碎混合物的压制和干燥标准实践

标准号

ASTM C1054-2003(2008)

发布日期

2003年

实施日期

废止日期

无

中国标准分类号

Q40

国际标准分类号

81.080 (Refractories)

发布单位

US-ASTM

适用范围

This practice is useful for producing uniform specimens of refractory plastics and ramming mixes for use in standard ASTM tests. Samples thus formed may be used for referee testing when setting specifications between producer and user. Forming parameters such as sample size, workability, and forming pressure should be agreed upon and specified in the report when referee testing.

This practice is applicable for preparing test specimens of various sizes. Note that 9 by 4x00BD; by 2x00BD; in. (228 by 114 by 64-mm) samples, because of their large cross-section, have a greater tendency to form flaws during pressing, handling, and drying than smaller cross-sectional samples.

Other tests for which these specimens may be used encompass, but are not limited to, the following ASTM standards: Method C 16, Test Methods C 20, Test Method C 113, Test Methods C 133, Test Method C 179, Test Method C 288, Test Method C 417, Test Method C 577, Test Method C 583, Test Method C 704, Test Methods C 830, Test Method C 832, Practice C 874, Test Method C 885, and Test Method C 914.

A purpose of this practice is to minimize flaws in pressed specimens. It is not intended to duplicate all field installation conditions.

Variations in workability as determined by Test Method C 181 can significantly affect the number of flaws contained in a specimen. For comparison testing between two laboratories, the workability level should be established by mutual agreement.

This practice is not intended for preparing specimens of basic ramming mixes, anhydrous tap-hole mixes, nor resin bonded mixes.

1.1 This practice covers the pressing and drying of chemically and nonchemically bonded aluminum-silicate and high alumina plastic and ramming mix refractory specimens classified in accordance with Classification C 673.

1.2 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.