This test method is used to determine the equilibrium rate of wear and coefficient of friction of materials in rubbing contact under useful operating conditions, that is, combinations of pressure and velocity that fall below the PV (pressure x00D7; velocity) limit of the test material. The user of this test method should determine to his own satisfaction whether the results of this test procedure correlate with field performance or other bench test machines. If the test conditions are changed, the wear rates may change and the relative value of one material with respect to another may also change.
Test conditions may be selected from Table 1.
The precision of wear measurement is relatively independent of test duration or amount of wear, but the precision of wear rate (calculation) improves with test duration and amount of wear. It is generally believed that useful wear rate precision requires the selection of a test duration sufficient to produce 0.1 mm (0.004 in.) of wear. Test durations will often be in the 50 to 4000-h range.
TABLE 1 Test ConditionsA
Rotational speed, rpm | Rubbing Velocity, ft/min (m/min) | Load, lb (kg), to Obtain PV, psi x00D7; ft/min (kg/cm 2 x00D7; m/min) at Selected Speeds | |||
---|---|---|---|---|---|
PV1 1250 (26.8) | PV2 2500 (53.6) | PV3 5000 (107.1) | PV4 10 000 (214.3) | ||
36 | 10 (3.05) | 25.0 (11.3) | 50.0 (22.7) | 100 (45.4) | 200 (90.7) |
180 | 50 (15.2) | 5.0 (2.3) | 10.0 (4.5) | 20.0 (9.1) | 40.0 (18.1) |
900 | 250 (76.2) | 1.0 (0.5) | 2.0 (0.9) | 4.0 (1.8) | 8.0 (3.6) |
A For many applications a wear rate exceeding 1.0 x00D7; 10x2212; 5 in./h (2.5 x00D7; 10x2212;7 m/h) is considered excessive. Typical wear rates for some commonly used materials at different PV levels are:
Acetal homopolymer at PV1: | 5 x00D7; 10x2212;6
ASTM D3702-1994(2009)相似标准推荐立式万能摩擦磨损试验机功能特点及操作说明立式万能摩擦磨损试验机是在一定的接触压力下,具有滚动、滑动或滑滚复合运动的摩擦形式,具有无级调速系统,可在极低速或高速条件下,用来评定润滑剂、金属、塑料、涂层、橡胶、陶瓷等材料的摩擦磨损性能。立式万能摩擦磨损试验机配备不同的摩擦副可分别进行球盘摩擦、销盘摩擦、止推圈摩擦、润滑剂摩擦,根据用户需求可提供球盘、球-三片、销-三柱、模拟凸轮、齿轮等多种摩擦副形式,功能覆盖全,用途广泛。... 摩擦磨损试验机常见标准常见的几种标准如下:GB/T12583-98 润滑剂极压性能测定法(四球机法)GB3142-82 润滑剂承载能力测定法(四球法)SH/T0189-92 润滑油抗磨性能测定法(四球机法)SH/T0202-92 润滑脂极压性能测定法(四球机法)SH/T0204-92 润滑脂抗磨性能测定法(四球机法)ASTM D3702-94 止推圈测定材料摩擦性能的试验方法ASTM G99-04 销盘检测材料摩擦性能的试验方法... ASTM D3702-1994(2009) 中可能用到的仪器设备