BS 2HR 5:2010
镍-铬-钛耐热铝坯、棒、铸件和部件用规范(镍基,Cr 19.5,Ti 0.4)
Specification for nickel-chromium-titanium heat-resisting alloy billets, bars, forgings and parts (nickel base, Cr 19.5, Ti 0. 4)
购买全文，请联系:
- 标准号
- BS 2HR 5:2010
- 发布
- 2010年
- 发布单位
- 英国标准学会
- 当前最新
- BS 2HR 5:2010
- 引用标准
- BS HR 100
- 被代替标准
- 09/30199933 DC-2009 BS HR 5:1972
- 适用范围
- This British Standard specifies requirements for nickel-chromiumtitanium heat-resisting alloy supplied in the following forms, and as parts. a) Bars and extruded sections for machining: annealed, designation HR 5A. b) Extruded sections for subsequent forming: softened, designation HR 5B. c) Billets and bars for forging: hot or cold worked and subsequently machined or ground, designation HR 5C. d) Forgings: annealed, designation HR 5D.
BS 2HR 5:2010相似标准
BS 3HR 1:2010 镍-铬-钛-铝耐热铝坯、棒、铸件和部件用规范(镍基,Cr 19.5, Ti 2.2,Al 1.4)
BS 2HR 403:2011 (Nickel base, Cr 19.5, Ti 0.4)镍-铬-钛耐热合金无缝管(镍基,Cr 19.5,Ti 0.4)规范
BS 2HR 1:1973 镍-铬-钛铝耐热合金坯锭、棒材、锻件和部件(镍基、Cr 19.5、Ti 2.2、Al 1.4)规范
2HR 1-1973 镍-铬-钛铝耐热合金坯锭、棒材、锻件和部件(镍基、Cr 19.5、Ti2.2、Al1.4)规范
2HR 2-1973 镍-铬-钛-铝耐热合金坯锭、棒材、锻件和部件(镍基、Cr 19.5、Co18.0、Ti25、Al1.5)规范
推荐
不同元素对不锈钢性能的影响
例如，欲使含18％铬的钢在常温下获得奥氏体组织，以锰和氮代镍的低镍不锈钢与元镍的铬锰氮不诱钢，目前已在工业中获得应用，有的已成功地代替了经典的18-8铬镍不锈钢。5、不锈钢中加钛或铌是为了防止晶间腐蚀。 6、钼和铜可以提高某些不锈钢的耐腐蚀性能。...
【材料课堂】不锈钢基础知识大汇总
2-1.铁素体钢含铬大于14％的低碳铬不锈钢，含铬大干27％的任何含碳量的铬不锈钢，以及在上述成分基础上再添加有钼、钛、铌、硅、铝、、钨、钒等元素的不锈钢，化学成分中形成铁素体的元素占绝对优势，基体组织为铁素。这类钢在淬火（固溶）状态下的组织为铁素体，退火及时效状态的组织中则可见到少量碳化物及金属间化合物。属于这一类的有Crl7、Cr17Mo2Ti、Cr25，Cr25Mo3Ti、Cr28等。...