BS EN ISO 6272-2:2011由英国标准学会 GB-BSI 发布于 2011-08-31,并于 2011-08-31 实施。
BS EN ISO 6272-2:2011 在中国标准分类中归属于: G51 涂料,在国际标准分类中归属于: 87.040 涂料和清漆。
* 在 BS EN ISO 6272-2:2011 发布之后有更新,请注意新发布标准的变化。
This part of ISO 6272 describes a method for evaluating the resistance of a dry film of paint, varnish or related product to cracking or peeling from a substrate when it is subjected to a deformation caused by a falling weight, dropped under standard conditions, acting on a small-area spherical indenter. NOTE The terms “impact” and “impact resistance” are used in the title and text of this part of ISO 6272, but an important characteristic of the apparatus used is that it should produce rapid deformation rather than a true impact. Because of the poor reproducibility of this test method, the method should be restricted to testing in only one laboratory when the results are expressed as numerical values. Interlaboratory agreement is improved when ranking is used in place of numerical values.
表1为最大压痕深度1.5 μ m时的试验结果,其中纳米硬度平均值为0.46GPa,而用传统硬度计算方法得到的硬度平均值为0.580GPa,这说明传统硬度计算方法在微纳米硬度测量时误差较大,其原因就是在微纳米硬度测量时,材料变形的弹性恢复造成残余压痕面积较小,传统方法使得计算结果产生了偏差,不能正确反映材料的硬度值。...
它还可以用于表面硬化层有效深度的测定,用于细小零件、小面积、薄材料、细线材、刀刃附近的硬度、电镀层及牙科材料硬度的测试。 关于产品(维氏与努氏)努氏硬度没有专门的硬度计,通常是与显微维氏硬度计共用,只要更换压头并且改变硬度值算法即可。...
英国的维克斯—阿姆斯特朗(Vickers-Armstrong)公司试制了第一台以此方法进行试验的硬度计。和布氏、洛氏硬度试验相比,维氏硬度试验测量范围较宽,从较软材料到超硬材料,几乎涵盖各种材料。维氏硬度的测定原理基本上和布氏硬度相同,也是根据压痕单位面积上的载荷来计算硬度值。所不同的是维氏硬度试验的压头是金刚石的正四棱锥体。...