ASTM D7249/D7249M-12
用长梁弯曲法测定夹层结构贴面性能的标准试验方法

Standard Test Method for Facing Properties of Sandwich Constructions by Long Beam Flexure

被代替

非常抱歉，我们暂时无法提供预览，您可以试试： 免费下载 ASTM D7249/D7249M-12 前三页，或者稍后再访问。

您也可以尝试购买此标准，
点击右侧 “立即购买” 按钮开始采购（由第三方提供）。

标准号

ASTM D7249/D7249M-12

发布

2012年

发布单位

美国材料与试验协会

替代标准

ASTM D7249/D7249M-12e1

当前最新

ASTM D7249/D7249M-20

 

 

适用范围

5. Significance and UseTop Bottom

5.1 Flexure tests on flat sandwich construction may be conducted to determine the sandwich flexural stiffness, the core shear strength, and shear modulus, or the facings??? compressive and tensile strengths. Tests to evaluate core shear strength may also be used to evaluate core-to-facing bonds.

5.2 This test method is limited to obtaining the strength and stiffness of the sandwich panel facings, and to obtaining load-deflection data for use in calculating sandwich beam flexural and shear stiffness using Standard Practice D7250/D7250M. Due to the curvature of the flexural test specimen when loaded, facesheet compression strength from this test may not be equivalent to the facesheet compression strength of sandwich structures subjected to pure edgewise (in-plane) compression.

5.3 Core shear strength and shear modulus are best determined in accordance with Test Method C273 provided bare core material is available. Test Method C393 may also be used to determine core shear strength. Standard Practice D7250/D7250M may be used to calculate the flexural and shear stiffness of sandwich beams.

5.4 This test method can be used to produce facing strength data for structural design allowables, material specifications, and research and development applications; it may also be used as a quality control test for bonded sandwich panels.

5.5 Factors that influence the facing strength and shall therefore be reported include the following: facing material, core material, adhesive material, methods of material fabrication, facing stacking sequence and overall thickness, core geometry (cell size), core density, adhesive thickness, specimen geometry, specimen preparation, specimen conditioning, environment of testing, specimen alignment, loading procedure, speed of testing, facing void content, adhesive void content, and facing volume percent reinforcement. Further, facing strength may be different between precured/bonded and co-cured facesheets of the same material.

Note 2???Concentrated forces on beams with thin facings and low density cores can produce results that are difficult to interpret, especially close to the failure point. Wider loading blocks and rubber pressure pads may assist in distributing the forces.

Note 3???To ensure that simple sandwich beam theory is valid, a good rule of thumb for the four-point bending test is the span length divided by the sandwich thickness should be greater than 20 (L/d gt; 20) with the ratio of facing thickness to core thickness less than 0.1 (t/c lt; ..........