5.1 This test method is applicable to dusts and powders, and provides a procedure for performing laboratory tests to evaluate hot-surface ignition temperatures of dust layers.
5.2 The test data can be of value in determining safe operating conditions in industrial plants, mines, manufacturing processes, and locations of material usage and storage.
5.3 Due to variation of ignition temperature with layer thickness, the test data at one thickness may not be applicable to all industrial situations (see Appendix X1). Tests at various layer thicknesses may provide a means for extrapolation to thicker layers, as listed in the following for pulverized Pittsburgh bituminous coal dust (2). Mathematical modeling of layer ignition at various layer thicknesses is described in Ref. (3).
Layer Thickness, mm | Hot-Surface Ignition Temperature, °C |
6.4 | 300 |
9.4 | 260 |
12.7 | 240 |
25.4 | 210 |
5.4 This hot plate test method allows for loss of heat from the top surface of the dust layer, and therefore generally gives a higher ignition temperature for a material than Test Method E771, which is a more adiabatic system.
5.5 This test method for dust layers generally will give a lower ignition temperature than Test Method E1491, which is for dust clouds. The layer ignition temperature is determined while monitoring for periods of minutes to hours, while the dust cloud is only exposed to the furnace for a period of seconds.
Note 1: Much of the literature data for layer ignition is actually from a basket in a heated furnace (4), known as the modified Godbert-Greenwald furnace test. Other......
织物与服装热防护性能测试方法 ASTM D4108明火法测试防护材料的热防护性能 这种标准从1995年以后就已经不再出版了,但后来的NFPA标准都是参照此标准而制订的。如图 3所示,将规格为100 mmX100 mm的织物试样水平放置在中间开有50 mmx50 mm小孔的试样架上,采用铜片热流计测量试样背面的温度,铜片热流计安装在一块绝热板内,其表面与绝热板表面平齐。...
说明: 1——受热面;3——隔热层; 2——外层;4——舒适层;图D.2 耐弯折性能试验装置 试验结论: 绘制测试试样的“温升—时间” 曲线和标准二度烧伤曲线, 标准二度烧伤曲线按式(D.1)绘制。 式中: T——温度,单位为摄氏度(℃); t——时间,单位为秒(s)。 ...
3、试验样品市售阻燃木材4、试验设备锥形量热仪(标准集团(香港)有限公司供应)4.1试验原理锥形量热仪的工作原理是采用氧消耗原理设计的测定材料燃烧放热的仪器,即大多数固体材料完全燃烧每消耗一单位质量的氧气所释放的热量基本相同(13.1mJ/kgO2±5%)。...
要求被测试样位于直径为(38±2)mm的火焰燃烧器上方,火焰与试样直接接触,位于织物背面的热流计测试织物背面温度上升12 ℃和24 ℃所需要的时间,测试原理如图1 所示。 火焰防护性能评价试验机的测试标准为ISO9151-1995标准,其采用铜片热流计表面温度上升12 ℃和24 ℃所需要的时间作为评价织物热防护性能的指标....
Copyright ©2007-2022 ANTPEDIA, All Rights Reserved
京ICP备07018254号 京公网安备1101085018 电信与信息服务业务经营许可证:京ICP证110310号