ISO 18852:2015
橡胶配合料.多点氮表面面积(NSA)和统计厚度表面面积(STSA)的测定
Rubber compounding ingredients - Determination of multipoint nitrogen surface area (NSA) and statistical thickness surface area (STSA)
- 标准号
- ISO 18852:2015
- 发布
- 2015年
- 发布单位
- 国际标准化组织
- 当前最新
- ISO 18852:2015
- 引用标准
- ISO 4652:2012 ISO 5794-1:2010 ISO 9277:2010 ISO 9298:1995
- 适用范围
- This International Standard specifies a method for the determination of the nitrogen surface area (NSA) of carbon blacks and other rubber compounding ingredients, like silicas and zinc oxides, based on the Brunauer, Emmett and Teller (BET) theory of gas adsorption using a multipoint determination as well as the determination of the statistical thickness surface area (STSA), otherwise known as the external surface area. STSA, however, is not applicable to silica and zinc oxide. The method can also be used for verifying “single-point” procedures described in ISO 4652 and other standards.
ISO 18852:2015相似标准
NF T45-023*NF ISO 18852:2015 橡胶配合料多点氮表面积（NSA）和统计厚度表面积（STSA）的测定
NF ISO 18852:2015 橡胶配合料 氮吸附面积测定(NSA)和多点法统计厚度面积(STSA)测定
GB/T 10722-2003 炭黑 总表面积和外表面积的测定氮吸附法
JIS K 6217-7:2008 橡胶工业用炭黑.基本特性.第7部分:橡胶配合材料. 多点氮表面面积(NSA)和统计学厚度表面面积(STSA)的测定
JIS K 6217-7:2013 橡胶工业用炭黑.基本特性.第7部分:橡胶配合料.多点氮表面面积(NSA)和统计学厚度表面面积(STSA)的测定
推荐
物理吸附 ▏比表面及孔径分析知识100问（第五章）
根据De Boer 理论和炭黑模型，在液氮温度下，氮吸附的相对压力（P/Po）与吸附层统计厚度 t 符合如下关系（ Carbon Black 模型） t = 0.088(P/Po)2+0.645(P/Po)+0.298模型指出，P/Po在0.2-0.5范围内(t大约在0.43-0.63)，氮吸附量对t作图时，对应于一条直线，由该直线的斜率(M)可计算出其外表面(STSA) ...
比表面积及孔径测试方法
比表面 测试方法 吸附法 低温氮吸附法 动态色谱法 (优势：比表面测试) 固体标样参比法 BET法 Langmuir法 统计吸附层厚度法 静态法 (优势：孔径测试) 重量法(很少使用) 容量法 BET法 (国标比表面测试方法) BET多点法 BET单点法 Langmuir法 统计吸附层厚度法 吸碘法(已很少使用) 吸汞法(已很少使用) 吸附其他分子方法 透气法(如博氏透气法，目前只应用于水泥行业) ...
比表面积的测试方法
统计吸附层厚度法主要用于计算外比表面；动态法仪器中有种常用的原理有直接对比法和多点BET法；动态法比表面仪，与其它分析仪器类似，影响其精度主要取决于检测方法、管路设计和是否具备操作完全自动化。 检测方法：氮吸附动态法国内比较成熟的比表面积测试方法，在比表面积研究和相关数据报告中，只有采用BET方法检测出来的结果才是真实可靠的，国内有很多仪器只能做直接对比法的检测，现在国内也被淘汰了。...