DS/ISO 34:1980
硫化橡胶. 撕裂强度的测定(裤形, 角形和新月形试片)

Rubber, vulcanized. Determination of tear strength (trouser, angle and crescent test pieces)

作废

非常抱歉，我们暂时无法提供预览，您可以试试： 免费下载 DS/ISO 34:1980 前三页，或者稍后再访问。

您也可以尝试购买此标准，
点击右侧 “购买” 按钮开始采购（由第三方提供）。

注意： 点击下载后，生成下载文件时间比较长，请耐心等待......

标准号

DS/ISO 34:1980

发布

1980年

发布单位

丹麦标准化协会

当前最新

DS/ISO 34:1980

 

 

适用范围

This International Standard specifies three test methods for the determination of the tear strength of vulcanized rubber, namely — Method A, based on the use of a trouser test piece; — Method B, based on the use of an angle test piece, with or without a nick of specified depth; — Method C, based on the use of a crescent test piece. The value of tear strength obtained depends on the shape of the test piece, speed of stretching and temperature of test. It may also be susceptible to grain effects in vulcanized rubber. Method A : using trouser test piece Method A, using the trouser test piece, is preferred because it is not sensitive to the length of the cut, unlike the other two test pieces in which the nick has to be very closely controlled. In addition, the results obtained are more easily related to the fundamental test properties of the material and are less sensitive to modulus effects (provided that the leg extension is negligible) and the rate of propagation of the tear is directly related to the rate of grip separation. However, all the methods are reasonably satisfactory in respect of reproducibility and practicability.[1]. Method B : Procedure (a) : Using angle test piece without nick The test is a combination of tear initiation and propagation. The stress is built up at the base of the angle until it is sufficient to initiate a tear and then further stresses propagate this tear. But it is only possible to measure the overall force required to rupture the test piece, and therefore, the force cannot be analysed into two components producing (1) initiation and (2) propagation. [3] Method B, procedure (b) : Using angle test piece with nick This test measures the force required to propagate a nick already produced in the test piece. The rate of propagation is not directly correlated with the jaw speed.［2］ Method C : Using crescent test piece This test also measures the force required to propagate a nick already produced in the test piece and the rate of propagation is not correlated with the jaw speed. NOTE — A separate method for the determination of tear strength of small test pieces of vulcanized rubbers (Delft test pieces) is specified in ISO 816.

DS/ISO 34:1980相似标准

推荐