DIN EN ISO 11782-2-2008
金属和合金的腐蚀.腐蚀疲劳试验.第2部分:使用预开裂样品的裂纹扩展测试

Corrosion of metals and alloys - Corrosion fatigue testing - Part 2: Crack propagation testing using precracked specimens (ISO 11782-2:1998); German version EN ISO 11782-2:2008

DIN EN ISO 11782-2-2008 发布历史

1.1 This part of ISO 11782 describes the fracture mechanics method of determining the crack growth rates of pre- existing cracks under cyclic loading in a controlled environment and the measurement of the threshold stress intensity factor range for crack growth below which the rate of crack advance falls below some defined limit agreed between parties. 1.2 This part of ISO 11782 provides guidance and instruction on corrosion fatigue testing of metals and alloys in aqueous or gaseous environments.

DIN EN ISO 11782-2-2008由德国标准化学会 DE-DIN 发布于 2008-08。

DIN EN ISO 11782-2-2008 在中国标准分类中归属于: H25 金属化学性能试验方法，在国际标准分类中归属于: 77.060 金属的腐蚀。

DIN EN ISO 11782-2-2008 发布之时，引用了标准

• ISO 7539-1-1987 金属与合金的腐蚀 应力腐蚀试验 第1部分:试验程序的通用指南

DIN EN ISO 11782-2-2008的历代版本如下：

• 2008年08月 DIN EN ISO 11782-2-2008 金属和合金的腐蚀.腐蚀疲劳试验.第2部分:使用预开裂样品的裂纹扩展测试

非常抱歉，我们暂时无法提供预览，您可以试试： 免费下载 DIN EN ISO 11782-2-2008 前三页，或者稍后再访问。

注意： 点击下载后，生成下载文件时间比较长，请耐心等待......

标准号

DIN EN ISO 11782-2-2008

发布日期

2008年08月

实施日期

废止日期

无

中国标准分类号

H25

国际标准分类号

77.060

发布单位

DE-DIN

引用标准

ISO 7539-1-1987

被代替标准

DIN EN ISO 11782-2-2007

适用范围

1.1 This part of ISO 11782 describes the fracture mechanics method of determining the crack growth rates of pre- existing cracks under cyclic loading in a controlled environment and the measurement of the threshold stress intensity factor range for crack growth below which the rate of crack advance falls below some defined limit agreed between parties. 1.2 This part of ISO 11782 provides guidance and instruction on corrosion fatigue testing of metals and alloys in aqueous or gaseous environments.

DIN EN ISO 11782-2-2008系列标准

谁引用了DIN EN ISO 11782-2-2008 更多引用