DIN EN ISO 11782-2:2008
金属和合金的腐蚀.腐蚀疲劳试验.第2部分:使用预开裂样品的裂纹扩展测试
Corrosion of metals and alloys - Corrosion fatigue testing - Part 2: Crack propagation testing using precracked specimens (ISO 11782-2:1998); German version EN ISO 11782-2:2008
- 标准号
- DIN EN ISO 11782-2:2008
- 发布
- 2008年
- 发布单位
- 德国标准化学会
- 替代标准
- DIN EN ISO 11782-2:2008-08
- 当前最新
- DIN EN ISO 11782-2:2008-08
- 引用标准
- ISO 7539-1:1987
- 被代替标准
- DIN EN ISO 11782-2:2007
- 适用范围
- 1.1 This part of ISO 11782 describes the fracture mechanics method of determining the crack growth rates of pre- existing cracks under cyclic loading in a controlled environment and the measurement of the threshold stress intensity factor range for crack growth below which the rate of crack advance falls below some defined limit agreed between parties. 1.2 This part of ISO 11782 provides guidance and instruction on corrosion fatigue testing of metals and alloys in aqueous or gaseous environments.
DIN EN ISO 11782-2:2008相似标准
推荐
金属材料应力腐蚀分析
（5）应力腐蚀的裂纹扩展速度一般在1 ×（10－9～10－6 ）m/s，跟疲劳断裂有点像，是缓慢渐进的，其远大于没有应力时的腐蚀速度，又远小于单纯力学因素引起的断裂速度。这种由亚临界扩展状况一直达到某一临界值，使剩余下的断面不能承受外载时，就突然发生断裂。而且裂纹部位存在孕育区、扩展区和瞬断区三部分。对于应力腐蚀，存在应力腐蚀开裂门槛值 K ISCC 。...
应力腐蚀断裂你知道有多少
一般认为纯金属不易发生应力腐蚀开裂，合金比纯金属更易发生应力腐蚀开裂。下表列出了各种合金风应力腐蚀开裂的环境介质体系，介质有特点：即金属或合金可形成纯化膜，弹介质中有有破坏纯化膜完整性的离子存在。而且介质中的有害物质浓度往往很低，如大气中微量的H2S和NH3可分别引起钢和铜合金的应力腐蚀开裂。空气中少量NH3是鼻子嗅不到的，却能引起黄铜的氨脆。...