GSO ISO 10587:2013由GSO 发布于 2013-12-31。
。
GSO ISO 10587:2013 金属和其他无机涂层 金属涂层和未涂层外螺纹制品和杆的残余脆化试验 倾斜楔块法的最新版本是哪一版？
最新版本是 GSO ISO 10587:2013 。
This International Standard specifies a method of determining, on a statistical basis, the probability of the existence of hydrogen embrittlement or degradation in: a) a batch of barrel electroplated, autocatalytic plated, phosphated or chemically processed threaded articles; b) a batch of rack plated threaded articles or rods. This International Standard is applicable to threaded articles and rod made from steel with an actual tensile strength ≥ 1 000 MPa (corresponding hardness values: 300 HV, 303 HB or 31 HRC) or to surface-hardened threaded articles or rods. It is not applicable to fasteners. The test method is carried out after hydrogen embrittlement relief heat treatment and may also be used for assessing differences in processing solutions, conditions and techniques. The test method has two main functions: a) when used with a statistical sampling plan it can be used for lot acceptance or rejection; b) it can be used as a control test to determine the effectiveness of the various processing steps including pre- and post-baking treatments to reduce the mobile hydrogen in the articles or rod. Although the test method is capable of indicating those articles that are embrittled to the extent defined in clause 2, it does not guarantee complete freedom from embrittlement. This International Standard does not relieve the plater, processor or manufacturer from imposing and monitoring suitable process control. NOTE 1 The use of inhibitors in acid pickling baths does not necessarily guarantee avoidance of hydrogen embrittlement. NOTE 2 Annex A provides guidance on sources of introduction of hydrogen into threaded articles.
Copyright ©2007-2022 ANTPEDIA, All Rights Reserved
京ICP备07018254号 京公网安备1101085018 电信与信息服务业务经营许可证：京ICP证110310号