During the period from June 30@1953 to Dec. 31@1954 some 117 experimental brazing alloys were prepared at the Handy and Harman research laboratories@ and evaluated as possible candidates for joining heat-conducting metal fins to Inconel tubing for service at temperatures in the order of 1400 to 1600 F where oxidation resistance oP the joint was mandatory. Alloys of gold-nickel-chromium@ and palladium-nickel base alloys with chromium and silicon were developed which can be used to join stainless steel to Inconel at brazing temperatures in the range of 1900 to 1950 F. The alloys can be torch brazed using flux@ or used without flux in a protective atmosphere. The resulting joints resist oxidation at 1600 F service temperature. It is still possible that with further development palladiumnickel base alloys with silicon-phosphorus-boron additions can be produced which will braze in the temperature range from 1850 to 1900 F. The report also contains a note on graphite brazing.
BULLETIN 30-1956由WRC - Welding Research Council 发布于 1956-09-01,并于 2012-09-24 实施。
非常抱歉,我们暂时无法提供预览,您可以试试: 免费下载 BULLETIN 30-1956 前三页,或者稍后再访问。
点击下载后,生成下载文件时间比较长,请耐心等待......
Copyright ©2007-2022 ANTPEDIA, All Rights Reserved
京ICP备07018254号 京公网安备1101085018 电信与信息服务业务经营许可证:京ICP证110310号