ASTM C1784-14
使用热流计法测量相变材料和产品储热性能的标准试验方法

Standard Test Method for Using a Heat Flow Meter Apparatus for Measuring Thermal Storage Properties of Phase Change Materials and Products

被代替

标准号

ASTM C1784-14

发布

2014年

发布单位

美国材料与试验协会

替代标准

ASTM C1784-20

当前最新

ASTM C1784-20

 

 

引用标准

ASTM C168 ASTM C518 ASTM E793 ASTM E967

适用范围

5.1 Materials used in building envelopes to enhance energy efficiency, including PCM products used for thermal insulation, thermal control, and thermal storage, are subjected to transient thermal environments, including transient or cyclic boundary temperature conditions. This test method is intended to enable meaningful PCM product classification, as steady-state thermal conductivity alone is not sufficient to characterize PCMs.

Note 3: This test method defines a dynamic test protocol for complex products or composites containing PCMs. Due to the macroscopic structure of these products or composites, conventional measurements using a Differential Scanning Calorimeter (DSC) as specified in E793 and E967, which use very small specimens, are not necessarily representative of the relationship between temperature and enthalpy of full-scale PCM products due to the specimen size limitation.

5.2 Dynamic measurements of the thermal performance of PCM products shall only be performed by qualified personnel with understanding of heat transfer and error propagation. Familiarity with the configuration of both the apparatus and the product is necessary.

5.3 This test method focuses on testing PCM products used in engineering applications, including in building envelopes to enhance the thermal performance of insulation systems.

5.3.1 Applications of PCM in building envelopes take multiple forms, including: dispersed in, or otherwise combined with, a thermal insulation material; a separate object implemented in the building envelope as boards or membranes containing concentrated PCM that operates in conjunction with a thermal insulation material. Both of these forms enhance the performance of the structure when exposed to dynamic, that is, fluctuating, boundary temperature conditions.

5.3.2 PCMs can be studied in a variety of forms: as the original “pure” PCM; as a composite containing PCM and other embedded materials to enhance thermal performance; as a product containing PCM or composite (such as micro- or macro-encapsulated PCM); or as a system, comprising arrays or assemblies of PCM products.

5.4 This test method describes a method of using a heat flow meter apparatus to determine key properties of PCM products, which are listed below. Engineers, architects, modelers, and others require these properties to accurately predict the in-situ performance of the products (2).

5.5 The objective is generally to conduct a test under temperature conditions that will induce a phase transition (for example, melting or freezing) in the PCM product during ......

强文推荐——塑料导热系数测试的方法和标准全解析

一般而言，除了泡沫塑料需要使用C518标准外，大部分塑料导热系数的最佳稳态方法是E1530，也就是防护热流计法。而特别软的黏性流体一样的热界面材料，需要测总体界面热阻，则选用D5470。非稳态法 稳态法对于中低导热系数的材料测量是非常简单而准确的，但是对于导热系数较大的金属和陶瓷材料而言，则非常麻烦。在20世纪60年代闪光法发明以前，金属材料是采用福布斯圆棒法进行稳态法测量的。...

平板热流计导热仪在绝热材料导热系数测量中应用

平板热流计导热仪在绝热材料导热系数测量中应用目前，绝热材料导热系数的测量主要使用护热平板法和平板热流计法两种方法，分别对应国标：GB/T10294-1988《绝热材料稳态热阻及有关特性的测定 防护热板法》；GB/T10295-1988《绝热材料稳态热阻及有关特性的测定（热流计法）》。...

高精度材料导热系数测试仪测试原理

可用于塑料、橡胶、保温材料等测试，广泛应用在大专院校、科研院所、质检、厂矿。参考标准：GB/T10295-2008（热材料稳态热阻及有关特性的测定热流计法）及ASTM C518-04用热流计法测定稳态热通量和热传递特性的试验方法。 ...

强文推荐——纳米石墨片与环氧树脂复合热界面材料的导热系数

图1 天然石墨热剥离之前和之后（c 轴膨胀可见其体积变化）的照片导热系数测试设备聚丙烯基复合材料的导热系数采用稳态法中的保护热流计法仪器测量，Fox 50，Lasercomp，TA 仪器。样品尺寸为直径50 mm，厚度1～20 mm， 遵循标准ASTM E1530。稳态法是直接测量方法，无须测量密度和比热，直接得到导热系数；样品更大，对于复合材料而言，更具代表性。...