This specification specifies the requirements, quality assurance, delivery preparation, instructions, etc. for hot-rolled and forged bars of superalloys. This specification applies to hot-rolled and forged high-temperature alloy bars (hereinafter referred to as bars) with a diameter of 20mm to 30mm for aerospace load-bearing parts.
GJB 3165A-2008 Referenced Document
GB/T 2 Fasteners.Ends of parts with external thread*, 2016-02-24 Update
GB/T 223.10 Methods for chemical analysis of iron,steel and alloy The cupferron separation-chrome azurol S photometric method for the determination of aluminium content
GB/T 223.3 Methods for chemical analysis of iron, steel and alloy--The diantipyrylmethane phosphomolybdate gravimetric method for the determination of phosphorus content
GB/T 223.41 Methods for chemical analysis of iron,steel and alloy--The anion-exchange separation-pyrogallol photometric method for the determination of tantalum content
GB/T 223.42 Methods for chemical analysis of iron,steel and alloy--The anion-exchange separation-bromopyrogallol red photometric method for the determination of tantalum content
GB/T 223.43 Iron,steel and alloy.Determination of tungsten content.Gravimetric method and spectrophotometric method*, 2008-05-13 Update
GB/T 223.46 Methods for chemical analysis of iron,steel and alloy--The flame atomic absorption spectrometric method for the determination of magnesium content
GB/T 223.47 Methods for chemical analysis of iron,steel and alloy. The carrier precipitation-molybdenum blue potometric method for the determination of antimony content
GB/T 223.48 Methods for chemical analysis of iron,steel and alloy--The semixylenol orange photometric method for the determination of bismuth content
GB/T 223.49 Methods for chemical analysis of iron,steel and alloy. Extraction separation-chlorophosphonazo mA spectrophotometric method for the determination of the total rare tarth content
GB/T 223.59 Iron,steel and alloy.Determination of phosphorus content.Bismuth phosphomolybdate blue spectrophotometic method and antimony phosphomolybdate blue spectruophotometric method*, 2008-08-19 Update
GB/T 223.60 Methods for chemical analysis of iron, steel and alloy--The perchloric acid dehydration gravimetric method for the determination of silicon content
GB/T 223.62 Methods for chemical analysis of iron, steel and alloy--The butyl acetate extraction photometric method for the determination of phosphorus content
GB/T 223.63 Iron, steel and alloy—Determination of manganese content—Sodium (potassium) periodate spectrophotometric method*, 2022-07-11 Update
GB/T 223.67 Iron,steel and alloy.Determination of sulfur content.Methylene blue spectrophotometric method*, 2008-05-13 Update
GB/T 223.68 Methods for chemical analysis of iron, steel and alloy. The potassium iodate titration method after combustion in the pipe furnace for the determination of sulfur content
GB/T 223.69 Iron,steel and alloy.Determination of carbon contents.Gas-volumetric method after combustion in the pipe furnace*, 2008-05-13 Update
GB/T 223.70 Iron,steel and alloy.Determination of iron contents. o-Phenanthroline spectrophotometric method*, 2008-05-13 Update
GB/T 223.71 Methods for chemical analysis of iron, steel and alloy. The gravimetric method after combustion in the pipe furnace for the determination of carbon content
GB/T 223.73 Iron,steel and alloy.Determination of iron contents. Titanium trichloride-potassium dichromate titration method*, 2008-05-13 Update
GB/T 223.8 Methods for chemical analysis of iron,steel and alloy The sodium fluoride separation-EDTA titration method for the determination of aluminium content
GB/T 223.9 Iron,steel and alloy.Determination of aluminium content.Chrome azurol S photometric method*, 2008-05-13 Update
GJB 3165A-2008 history
2020GJB 3165A-2020 Specification for hot-rolled and forged bars of high-temperature alloys for aerospace load-bearing parts
2008GJB 3165A-2008 Specification for hot-rolled and forged superalloy bars for aviation load-bearing parts
1998GJB 3165-1998 Specification for hot-rolled and forged bars of high-temperature alloys for aerospace load-bearing parts