ASTM F3213-17
添加剂制造标准&x2013；成品零件属性–；通过粉末床熔合钴-28铬-6钼的标准规范

Standard for Additive Manufacturing – Finished Part Properties – Standard Specification for Cobalt-28 Chromium-6 Molybdenum via Powder Bed Fusion

标准号

ASTM F3213-17

发布

2017年

发布单位

美国材料与试验协会

当前最新

ASTM F3213-17

 

 

引用标准

ASME B46.1 ASTM A484/A484M ASTM B213 ASTM B214 ASTM B243 ASTM B311 ASTM B822 ASTM B855 ASTM B964 ASTM D3951 ASTM E10 ASTM E1019 ASTM E11 ASTM E1417 ASTM E1450 ASTM E1473 ASTM E1742/E1742M ASTM E18 ASTM E1820 ASTM E1941 ASTM E21 ASTM E23 ASTM E2368 ASTM E238 ASTM E29 ASTM E3 ASTM E354 ASTM E384 ASTM E399 ASTM E407 ASTM E466 ASTM E606 ASTM E647 ASTM E8/E8M ASTM E9 ASTM F1377 ASTM F1537 ASTM F2924 ASTM F2971 ASTM F3049 ASTM F3122 ASTM F75 ISO 1099 ISO 12108 ISO 12111 ISO 12135 ISO 12737 ISO 13485 ISO 148-1 ISO 19819 ISO 4545 ISO 6506-1 ISO 6507-1 ISO 6508 ISO 6892-1 ISO 6892-2 ISO 9001 ISO 9044 SAE AMS2248 SAE AMS2269 SAE AMS2774 SAE AMS5599 SAE AMS5894

适用范围

1.1 本规范涵盖通过基于激光和电子束的全熔体粉末床熔合工艺增材制造的化学成分与 UNS R30075 类似的钴 28 铬 6 钼合金部件。通过这些工艺生产的部件通常用于需要类似于铸造或锻造产品的机械性能的应用。按照此规格制造的部件通常（但不一定）通过机械加工、磨削、放电加工 (EDM)、抛光等进行后处理，以实现所需的表面光洁度和关键尺寸。
1.2 本规范旨在供增材制造的钴 28 铬 6 钼合金部件的购买者或生产者（或两者）使用，以定义要求并确保部件性能。
1.3 建议用户使用本规范作为获得组件的基础，这些组件将满足委员会成员协商一致制定和修订的最低验收要求。
1.4 被认为比第 1-22 节中的要求更严格的用户要求可以通过在采购订单中添加一项或多项补充要求来满足，其中可能包括但不限于补充要求 S1-S14 中列出的要求。
1.5 以 SI 单位表示的数值应被视为标准。其他单位仅供参考。
1.6 本规范中钴 28 铬 6 钼合金成分的化学成分要求类似于规范 F1537 合金 1 和 2（锻造钴 28 铬 6 钼）和规范 F75（铸造钴 28 铬 6 钼）。
1.7 本国际标准是根据世界贸易组织贸易技术壁垒（TBT）委员会发布的《关于制定国际标准、指南和建议的原则的决定》中确立的国际公认的标准化原则制定的。