81.060.10 原料 标准查询与下载

ASTM C866-11(2022) 陶瓷白瓷粘土过滤率的标准试验方法

1.1 This test method covers the determination of the rate at which a layer of clay-water paste is formed from a clay-water slip under pressure filtration. The filtration rate is directly related to such whiteware operations as filter pressing, slip casting, and drying of ware in which water permeability through a clay-water paste is the controlling mechanism. 1.2 A straight-line relationship exists between the time of filter pressing and the square of the thickness of the paste layer. The filtration rate is directly related to the filter press pressure and the void fraction of the paste layer, and is inversely related to the square of the clay surface area, the ratio of solids to liquid in the slip, and the viscosity of water at the testing temperature. 1.3 The values stated in acceptable metric units are to be regarded as the standard. The values given in parentheses are for information only. 1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

Standard Test Method for Filtration Rate of Ceramic Whiteware Clays

ASTM C325-07(2022) 陶瓷白瓷粘土的湿筛分析标准指南

1.1 This guide covers the wet sieve analysis of ceramic whiteware clays. This guide is intended for use in testing shipments of clay as well as for plant control tests. 1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

Standard Guide for Wet Sieve Analysis of Ceramic Whiteware Clays

KS L 1614-2021 激光衍射法测定细陶瓷原料粉末的粒度分布

Determination of particle size distributions for fine ceramic raw powders by laser diffraction method

KS L 4007-2021 粘土化学分析方法

Methods for chemical analysis of clay

KS L 5506-2021 未烧粘土断裂模量的测试方法

Testing method for modulus of rupture of unfired clays

KS L 4005-2021 非塑性陶瓷材料的筛分分析

Sieve analysis of nonplastic ceramic materials

KS L 1612-2021 精细陶瓷用碳化硅细粉化学分析方法

Methods for chemical analysis of fine silicon carbide powders for fine ceramics

T/CCIA 0007-2021 陶瓷用乌兰茶晶石粉

本标准主要规定了产品的常规八大元素，硅、铝、钙、镁、钾、钠、铁、钛、灼减量，以及稀土元素、硒元素、放射性等检测项目；产品外观的物理状态检测。

Wu Lan Cha Jing Mixed Feldspar for ceramics

DIN 51102:2021 陶瓷材料试验.耐浓酸性的测定

This document specifies a method for determining the resistance of ceramic materials to sulfuric acid on lumpy test material.

Testing of ceramic material - Determination of concentrated acid resistance

GOST 9169-2021 陶瓷工业用粘土材料 分类

Clay raw materials for the ceramic industry. Classification

GOST 7031-2021 精细陶瓷用石英砂

Quartzy sand for fine ceramics. Specifications

KS L 9001-2020 石膏巴黎模具陶器

Plaster of paris mold for pottery

KS L 9002-2020 陶器石膏的物理测试方法

Method of physical test for plaster of paris mold for pottery

ASTM C721-20 通过透气度估算氧化铝和二氧化硅粉末的平均粒径的标准测试方法

1.1 These test methods cover the estimation of the average particle size in micrometres of alumina and silica powders using an air permeability method. The test methods are intended to apply to the testing of alumina and silica powders in the particle size range from 0.2 to 75 µm. 1.2 The values stated in SI units are to be regarded as standard, with the exception of the values for density and the mass used to determine density, for which the use of the gram per cubic centimetre (g/cm3 ) and gram (g) units is the longstanding industry practice; and the units for pressure, cm H2O—also long-standing practice. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

Standard Test Methods for Estimating Average Particle Size of Alumina and Silica Powders by Air Permeability

T/CBCSA 24-2020 伊利石型水洗瓷土

本标准规定了伊利石型水洗瓷土的术语和定义，分级、要求、试验方法、检验规则、标志、包装、运输和贮存。

Illite type washed porcelain clay

T/FSCIA 0011-2020 陶瓷砖坯体原料要求和检测方法

本标准规定了陶瓷砖坯体原料的术语和定义、要求、检测方法。 本标准适用于陶瓷砖坯体原料的物理性能和化学成分检测。 主要技术内容包括外观质量、含水率、筛余量、干燥抗折强度、线收缩率、白度、粘度、酸碱度、化学成分等内容

Raw material requirements and testing methods for ceramic tile body

T/FSCIA 0001-2020 建筑陶瓷用硅酸锆

主要技术内容包括外观质量、含水率、放射性、化学成分和物理性能。

Zirconium silicate for building ceramics

T/FSCIA 0010-2020 陶瓷砖坯体原料取样方法

本标准规定了陶瓷砖坯体原料取样方法的术语和定义、取样总则、取样工具、取样点的选取、取样 步骤及取样操作、取样量、样品的制备、样品单、包装和贮存。 本标准适用于陶瓷砖坯体原料的取样。 主要技术内容包括取样总则、取样工具、取样点的选取、取样 步骤及取样操作、取样量、样品的制备、样品单、包装和贮存等内容。

Sampling method of raw materials for ceramic tile body

ASTM C1070-01(2020) 通过激光散射测定氧化铝或石英的粒度分布的标准测试方法

1.1 This test method covers the determination of particle size distribution of alumina or quartz using laser lightscattering instrumentation in the range from 0.1 to 500 µm. 1.2 The procedure described in this test method may be applied to other nonplastic ceramic powders. It is at the discretion of the user to determine the method’s applicability. 1.3 This test method applies to analysis using aqueous dispersions. 1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.5 Quartz has been classified by IARC as a Group I carcinogen. For specific hazard information in handling this material, see the supplier’s Material Safety Data Sheet. 1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

Standard Test Method for Determining Particle Size Distribution of Alumina or Quartz by Laser Light Scattering

T/FSCIA 0012-2019 建筑卫生陶瓷用黑泥

建筑卫生陶瓷原材料粘土类中黑泥的术语和定义、技术要求、试验方法、检验规则、 标识、包装、运输和贮存。其中技术要求包括：外观质量、化学成分和物理性能、烧后白度、含水率、筛余量、干燥抗折强度、线收缩率、粘度、酸碱度、可塑性指数等指标。

Black clay for building and sanitary ceramics